Very thin films of tellurium, with mean thickness up to 100 A, were deposited in ultra high vacuum at room temperature on a Si(100) 2 x 1 surface, and were exposed to different amounts of O-2 and to the atmosphere. Ultraviolet photoelectron spectroscopy, X-ray photoelectron spectroscopy and low energy electron diffraction spectroscopy were performed in order to investigate the reactivity of the Te/Si(100) system towards oxygen. The Si(100) 2 x 1 surface is found to chemisorb O-2 and to saturate with approximate to 500 Langmuir. In contrast, the tellurium films are not active either towards oxygen or towards the atmosphere for a few minutes: no changes are detectable in the UPS and XPS spectra and LEED patterns of samples with the Si(100) surface completely covered by Te. With deposition of 1 A of tellurium the silicon substrate is not completely covered, and the sample can chemisorb a lower amount of oxygen with respect to the pure Si(100) 2 x 1 surface. The tellurium film thus acts as a protective barrier against the oxidation of silicon.

REACTIVITY TOWARDS OXYGEN OF TE/SI(100) SURFACES INVESTIGATED BY ULTRAVIOLET PHOTOELECTRON-SPECTROSCOPY, X-RAY PHOTOELECTRON-SPECTROSCOPY AND LOW-ENERGY-ELECTRON DIFFRACTION SPECTROSCOPY

LOZZI, Luca;PASSACANTANDO, MAURIZIO;
1995-01-01

Abstract

Very thin films of tellurium, with mean thickness up to 100 A, were deposited in ultra high vacuum at room temperature on a Si(100) 2 x 1 surface, and were exposed to different amounts of O-2 and to the atmosphere. Ultraviolet photoelectron spectroscopy, X-ray photoelectron spectroscopy and low energy electron diffraction spectroscopy were performed in order to investigate the reactivity of the Te/Si(100) system towards oxygen. The Si(100) 2 x 1 surface is found to chemisorb O-2 and to saturate with approximate to 500 Langmuir. In contrast, the tellurium films are not active either towards oxygen or towards the atmosphere for a few minutes: no changes are detectable in the UPS and XPS spectra and LEED patterns of samples with the Si(100) surface completely covered by Te. With deposition of 1 A of tellurium the silicon substrate is not completely covered, and the sample can chemisorb a lower amount of oxygen with respect to the pure Si(100) 2 x 1 surface. The tellurium film thus acts as a protective barrier against the oxidation of silicon.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11697/11147
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 4
social impact