Microstructure characterization of sol-gel prepared MoO3-TiO2 thin films for oxygen gas sensors

Binary metal-oxide MoO3-TiO2 films have been prepared using the sol-gel technique. The thin films were annealed at several temperatures including 400, 450, 500, 550, and 600 degreesC for 1 h. The morphology, crystalline structure, and chemical composition of the films have been analyzed using scanning electron microscopy (SEM) and atomic force microscopy, x-ray diffraction (XRD), Rutherford backscattering spectroscopy (RBS), and x-ray photoelectron spectroscopy (XPS) techniques. The SEM analysis showed that there are two different sizes of grains in the films annealed at temperatures of 400, 450, 500, and 550 degreesC. One grain type is small with 20-100 nm; the other is a large grain type several micrometers in length. The XRD analysis revealed that the films annealed at 400 degreesC were a mixture of orthorhombic and hexagonal MoO3 phases. The films annealed at 450 degreesC showed an increase in the hexagonal phase. A preferential orientation growth along the (100) plane of the hexagonal phase and the (010) plane of the orthorhombic phase has been found in both samples. RES and XPS analysis showed that the films were stoichiometric. When the annealing temperature was increased beyond 500 degreesC, the concentration ratio of MoO3-TiO2 decreased due to the evaporation of MoO3. For the study of the electrical and gas sensing properties, the films were deposited on sapphire substrates with interdigital electrodes on the frontside and a Pt heater on the backside. The MoO3-TiO2 thin films are sensitive to oxygen gas. The film has exhibited the O-2 response (S = R-g/R-b) of 2.1, 8.1 and 80 for 120, 1000, and 10000 ppm concentration of O-2, respectively. (C) 2001 American Vacuum Society. RI li , yongxiang/C-5059-2009; Russo, Salvy/E-5837-2011