Room temperature gas sensing properties of chemically exfoliated black phosphorus (BP) to oxidizing (NO2, CO2) and reducing (NH3, H2, CO) gases in a dry air carrier have been reported. To study the gas sensing properties of BP, chemically exfoliated BP flakes have been drop casted on Si3N4 substrates provided with Pt comb-type interdigitated electrodes in N2 atmosphere. Scanning electron microscopy and x-ray photoelectron spectroscopy characterizations show respectively the occurrence of a mixed structure, composed of BP coarse aggregates dispersed on BP exfoliated few layer flakes bridging the electrodes, and a clear 2p doublet belonging to BP, which excludes the occurrence of surface oxidation. Room temperature electrical tests in dry air show a p-type response of multilayer BP with measured detection limits of 20 ppb and 10 ppm to NO2 and NH3 respectively. No response to CO and CO2 has been detected, while a slight but steady sensitivity to H2 has been recorded. The reported results confirm, on an experimental basis, what was previously theoretically predicted, demonstrating the promising sensing properties of exfoliated BP.

Exfoliated black phosphorus gas sensing properties at room temperature

DONARELLI, MAURIZIO;OTTAVIANO, LUCA;GIANCATERINI, LUCA;FIORAVANTI, GIULIA;PERROZZI, FRANCESCO;CANTALINI, Carlo
2016-01-01

Abstract

Room temperature gas sensing properties of chemically exfoliated black phosphorus (BP) to oxidizing (NO2, CO2) and reducing (NH3, H2, CO) gases in a dry air carrier have been reported. To study the gas sensing properties of BP, chemically exfoliated BP flakes have been drop casted on Si3N4 substrates provided with Pt comb-type interdigitated electrodes in N2 atmosphere. Scanning electron microscopy and x-ray photoelectron spectroscopy characterizations show respectively the occurrence of a mixed structure, composed of BP coarse aggregates dispersed on BP exfoliated few layer flakes bridging the electrodes, and a clear 2p doublet belonging to BP, which excludes the occurrence of surface oxidation. Room temperature electrical tests in dry air show a p-type response of multilayer BP with measured detection limits of 20 ppb and 10 ppm to NO2 and NH3 respectively. No response to CO and CO2 has been detected, while a slight but steady sensitivity to H2 has been recorded. The reported results confirm, on an experimental basis, what was previously theoretically predicted, demonstrating the promising sensing properties of exfoliated BP.
File in questo prodotto:
File Dimensione Formato  
2dm_3_2_025002_2016.pdf

non disponibili

Descrizione: pdf dell'articolo pubblicato
Tipologia: Documento in Versione Editoriale
Licenza: Dominio pubblico
Dimensione 1.03 MB
Formato Adobe PDF
1.03 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11697/106692
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 100
  • ???jsp.display-item.citation.isi??? 98
social impact