Effect of airborne particle abrasion on microtensile bond strength of total-etch adhesives to human dentin

Aim of this study was to investigate a specific airborne particle abrasion pretreatment on dentin and its effects on microtensile bond strengths of four commercial total-etch adhesives. Midcoronal occlusal dentin of extracted human molars was used. Teeth were randomly assigned to 4 groups according to the adhesive system used: OptiBond FL (FL), OptiBond Solo Plus (SO), Prime & Bond (PB), and Riva Bond LC (RB). Specimens from each group were further divided into two subgroups: control specimens were treated with adhesive procedures; abraded specimens were pretreated with airborne particle abrasion using 50 μm Al2O3before adhesion. After bonding procedures, composite crowns were incrementally built up. Specimens were sectioned perpendicular to adhesive interface to producemultiple beams, which were tested under tension until failure.Data were statistically analysed. Failure mode analysis was performed. Overall comparison showed significant increase in bond strength (p < 0.001) between abraded and no-abraded specimens, independently of brand. Intrabrand comparison showed statistical increase when abraded specimens were tested compared to no-abraded ones, with the exception of PB that did not show such difference. Distribution of failure mode was relatively uniformamong all subgroups. Surface treatment by airborne particle abrasion with Al2O3particles can increase the bond strength of total-etch adhesives.