The effect of the annealing temperature Tann on the magnetic properties of cobalt ferrite nanoparticles embedded in an amorphous silica matrix (CoFe2O4/SiO2), synthesized by a sol‐gel auto‐combustion method, was investigated by magnetization and AC susceptibility measurements. For samples with 15% w/w nanoparticle concentration, the particle size increases from ~2.5 to ~7 nm, increasing Tann from 700 to 900 °C. The effective magnetic anisotropy constant (Keff) increases with decreasing Tann, due to the increase in the surface contribution. For a 5% w/w sample annealed at 900 °C, Keff is much larger (1.7 × 106 J/m3) than that of the 15% w/w sample (7.5 ×105 J/m3) annealed at 700 °C and showing comparable particle size. This indicates that the effect of the annealing temperature on the anisotropy is not only the control of the particle size but also on the core structure (i.e., cation distribution between the two spinel sublattices and degree of spin canting), strongly affecting the magnetocrystalline anisotropy. The results provide evidence that the magnetic anisotropy comes from a complex balance between core and surface contributions that can be controlled by thermal treatments.

Magnetocrystalline and surface anisotropy in cofe2o4 nanoparticles

D'orazio F.
;
2020-01-01

Abstract

The effect of the annealing temperature Tann on the magnetic properties of cobalt ferrite nanoparticles embedded in an amorphous silica matrix (CoFe2O4/SiO2), synthesized by a sol‐gel auto‐combustion method, was investigated by magnetization and AC susceptibility measurements. For samples with 15% w/w nanoparticle concentration, the particle size increases from ~2.5 to ~7 nm, increasing Tann from 700 to 900 °C. The effective magnetic anisotropy constant (Keff) increases with decreasing Tann, due to the increase in the surface contribution. For a 5% w/w sample annealed at 900 °C, Keff is much larger (1.7 × 106 J/m3) than that of the 15% w/w sample (7.5 ×105 J/m3) annealed at 700 °C and showing comparable particle size. This indicates that the effect of the annealing temperature on the anisotropy is not only the control of the particle size but also on the core structure (i.e., cation distribution between the two spinel sublattices and degree of spin canting), strongly affecting the magnetocrystalline anisotropy. The results provide evidence that the magnetic anisotropy comes from a complex balance between core and surface contributions that can be controlled by thermal treatments.
File in questo prodotto:
File Dimensione Formato  
nanomaterials-10-01288 Peddis.pdf

accesso aperto

Tipologia: Documento in Post-print
Licenza: Dominio pubblico
Dimensione 1.45 MB
Formato Adobe PDF
1.45 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11697/165394
Citazioni
  • ???jsp.display-item.citation.pmc??? 3
  • Scopus 22
  • ???jsp.display-item.citation.isi??? 23
social impact