ETS-10 and ETS-4 microporous materials were synthesized in presence of tetralkylammonium (TAA) ions from gels of molar composition w Na2O–0.10 TAABr–1 SiO2–z TiO2–0.6 KF–1.28 w HCl–39.5 H2O with TAA = tetramethyl-, tetraethyl-, tetrapropyl- and tetrabutyl-ammonium in hydrothermal conditions at 190 °C. The TAA ions enter the microporous channel of ETS-10, while they cannot penetrate the void spaces of ETS-4. The ETS-10 microcrystals are all cubic, while the ETS-4 crystals are laminar and irregular. The microporous volume of ETS-10 is equal to 0.11–0.13 cm3 g−1, the microporous volume of ETS-4 is very small, 0.002–0.008 cm3 g−1. The ion exchange of Cs+, Cd++, Pb++ and Hg++ ions using their corresponding nitrates show kinetic effects, i.e. the efficiency of ion exchange is higher at 1 than 2 h, the thermodynamic equilibrium. For ETS-10, partially dehydrated cations intervene in the ion exchange, while for ETS-4 well dehydrated ions can only penetrate the available pores.

Kinetic and thermodynamic effects during the adsorption of heavy metals on ETS-4 and ETS-10 microporous materials

Aloise A.;
2016-01-01

Abstract

ETS-10 and ETS-4 microporous materials were synthesized in presence of tetralkylammonium (TAA) ions from gels of molar composition w Na2O–0.10 TAABr–1 SiO2–z TiO2–0.6 KF–1.28 w HCl–39.5 H2O with TAA = tetramethyl-, tetraethyl-, tetrapropyl- and tetrabutyl-ammonium in hydrothermal conditions at 190 °C. The TAA ions enter the microporous channel of ETS-10, while they cannot penetrate the void spaces of ETS-4. The ETS-10 microcrystals are all cubic, while the ETS-4 crystals are laminar and irregular. The microporous volume of ETS-10 is equal to 0.11–0.13 cm3 g−1, the microporous volume of ETS-4 is very small, 0.002–0.008 cm3 g−1. The ion exchange of Cs+, Cd++, Pb++ and Hg++ ions using their corresponding nitrates show kinetic effects, i.e. the efficiency of ion exchange is higher at 1 than 2 h, the thermodynamic equilibrium. For ETS-10, partially dehydrated cations intervene in the ion exchange, while for ETS-4 well dehydrated ions can only penetrate the available pores.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11697/176589
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 28
  • ???jsp.display-item.citation.isi??? 22
social impact